| Customization: | Available |
|---|---|
| Certification: | CE, ISO9001: 2000 |
| Automatic Grade: | Automatic |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Top Professional High Quality Autoclave Aerateed Concrete(AAC) Block Making Machine
ShanDong SUNITE Machinery Group Co., Ltd, established in October, 1998, is a Chinese manufacturer of dedicated in AAC block making machine production line. The registered captical is more than REB 10 million and employees is more than 500 including 6 senior engineers and 28 intermediate engineers. It's the first professional manufacturer in China specialized in the manufacturer of autoclaved aerated concrete block equipment, aerated concrete wall panel equipement, steam-cured and autoclaved brick equipment.
Top Professional High Quality Autoclave Aerateed Concrete(AAC) Block Making Machine
Top Professional High Quality Autoclave Aerateed Concrete(AAC) Block Making Machine
1.Improved thermal efficiency reduces the heating and cooling load in buildings.
2.Porous structure allows for superior fire resistance.
3.Workability allows accurate cutting, which minimizes the generation of solid waste during use.
4.Resource efficiency gives it lower environmental impact in all phases of its life cycle, from processing of raw materials to the disposal of waste.
5.Light weight saves cost & energy in transportation, labor expenses, and increases chances of survival during seismic activity.
6.Environmentally Friendly: When used, it helps to reduce at least 30% of environmental waste as opposed to going with traditional concrete. There is a decrease of 50% of greenhouse gas emissions. When possible, using autoclaved aerated concrete is a better choice for the environment.
7.Energy Saver: It is an excellent property that makes it an excellent insulator and that means the interior environment is easier to maintain. When it is used, there is usually not a need for any supplementary insulation.
8. Light Weight: 400~700kg/m3.
9. High Intensity: 3.5~10.0Mpa.
10. Good Thermal Insulation Property: 0.1~0.20W/(m · k).
The size depend on you (aac block machine)
Fly ash style aac block raw material proportion(aac block machine):
|
Parameter Name |
Parameter Value |
|
Sand |
55-65% |
|
Cement |
10-20% |
|
Lime |
20-30% |
|
Gypsum |
2-3% |
|
Aluminum powder paste |
8 |
|
Water & material rate |
0.65-0.75 |
|
Casting temperature |
35-38°C |
|
Aluminum mixing time |
30-40s |
Sand style aac block raw material proportion(aac block machine):
|
Parameter Name |
Parameter Value |
|
Sand |
55-65% |
|
Cement |
10-20% |
|
Lime |
20-30% |
|
Gypsum |
2-3% |
|
Aluminum powder paste |
8 |
|
Water & material rate |
0.65-0.75 |
|
Casting temperature |
35-38°C |
|
Aluminum mixing time |
30-40s |
Main Process Flow of Autoclaved Aerated Concrete aac Block Making Machine:
1. Raw material: Store the fly-ash (tailings etc), lime and gypsum after milling into the needed fineness (200 mesh)
2. Mixing the fly-ash, cement, lime, gypsum and water in the pot after batching.
3. Increase the slurry temperature to 40-50 centigrade by steam, and mill with aluminum powder for 1min.
4. Pour the slurry into the mould, and still in the curing room for frothing in 2-2.5h.
5. Cut it into needed size by the cutter after the slurry reach the cutting intensity, and place the block on the trolley cart.
6. Autoclaved curing after the trolley cart enter the autoclave (vacuum, raise the pressure, keep the pressure, reduce the pressure),keeping the constant pressure 1.2MPa. The whole process needs about 8 hours.
7. The products out of the autoclave are placed in a stack. We can recycle the scrap and the waste water from the whole production.
aac block machine
1. Product weight is according to 600kg/m3 to control.
2.Annual capacity 200,000 m3
3.Set raw material proportion: cement 6.5%, raw lime 23%, fay ash 68%, gypsum3%,aluminum paste powder 350g/m3
4. water and material rate 0,631
5.one mould product 2.88 m3
6. casting slurry cycle time 5-6 minutes, cut cycle 5 minutes
7.casting slurry temperature 38-42 degree
8.body quiet stop, Timeis 1.5-2.5 hours, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa.
9.Steam curing cycle time, come in and out avtoclave about 0.5 hours, steam curing cycle time about is 6 hours/ 1.6Mpa, total 6 .5 hours.
aac block machine
Autoclaved Aerated Concrete aac Block Making Machine
chinese manual aac block manufacturer with autoclave and cutting machine
chinese manual aac block manufacturer with autoclave and cutting machine
chinese manual aac block manufacturer with autoclave and cutting machine
Thanks for your attention, I am looking forward to talking more details with you.
){kind=link}